SEAMLESS STEEL GAS CYLINDERS

SEAMLESS STEEL GAS CYLINDER

Brand: KAIGEN, LEO

Outside Diameter: 32 mm, 51 mm, 54 mm, 62 mm, 68 mm, 83 mm, 89 mm, 102 mm, 104 mm, 105 mm, 108 mm, 114 mm, 123 mm, 127 mm, 133 mm, 140 mm, 116 mm, 152 mm, 159 mm, 165 mm, 168 mm, 178 mm, 180 mm, 204 mm, 219 mm, 223 mm, 229 mm, 232 mm, 245 mm, 267 mm, 273 mm, 279 mm, 299 mm, 325 mm, 351 mm, 356 mm, 377 mm, 406 mm, 426 mm, 465 mm, 467 mm, 470 mm, 500 mm, etc.

Water Capacity: 0.09 L to 410 L

Volume: 0.0135 m³ to 172.2 m³

Material: Seamless Steel (37Mn, 34CrMo4, 30CrMo, 4130X, 35CrMo)

Working Pressure: 900 Psi, 2015 Psi, 2130 Psi, 2175 Psi, 2265 Psi, 2300 Psi, 2400 Psi, 2900 Psi, 3000 Psi, 5000 Psi, 69 Bar, 150 Bar, 154 Bar, 166.7 Bar, 167 Bar, 173 Bar, 174 Bar, 176 Bar, 184 Bar, 200 Bar, 210 Bar, 230 Bar, 255 Bar, 262 Bar, 275 Bar, 300 Bar, 330 Bar, 350 Bar, 377 Bar, 400 Bar, 416 Bar, 690 Bar, 0.7 MPa, 3 MPa, 14.7 MPa, 15 MPa, 17 MPa, 17.2 MPa, 18 MPa, 20 MPa, 22 MPa, 22.6 MPa, 25 MPa, 30 MPa, 31.5 MPa, 33 MPa, 35 MPa, 40 MPa, 42 MPa, 69 MPa, 70 MPa, etc.

Production Process: Spun-tube, Billet-pierced

Standard and Certification: ASME, DOT, DOT/UN ISO, TPED, CE, PED, UN ISO, EN ISO, UL, TC, AS/NZS, ISO (including ISO 9809-1, ISO 9809-2, ISO 9809-3), Rho, EN, CU-TR, EAC, GOST, KGS, KR, KSB, JIS B, KHK, CDG & TPE, IS, PESO, AS, AD, BS, PD, ADR/RID, GB, CLASSIFICATION SOCIETY STANDARDS (ABS, BV, KR, LR, DNV, GL, NK, RINA, RS, CCS, CFR)

Cylinder Bottom Shape: convex bottom or concave bottom

KAIGEN ADVANTAGES:

1. Cold Spinning Cylinder Thinning Technology

(1) The cylinder body structure is denser and the fiber structure distribution is more reasonable and orderly.

(2) The wall thickness is uniform and the tolerance can reach ±6% of the wall thickness.

(3) The surface is smooth and the roughness value does not exceed 12.5 μm.

(4) The metallographic structure is better than the traditional process cylinders.

2. Special Hot Spinning Bottom Shrinking Process

(1) Using an infrared temperature sensor to accurately control the furnace temperature ± 8 °C.

(2) The auxiliary heating gas gun is controlled by a servo motor to achieve the perfect fusion of the bottom of the cylinder.

(3) The special forward and reverse spinning processing technology ensures the thickness of the bottom landing point and the center point of the cylinder, while increasing the thickening of the bottom of the cylinder.

3. Special production and processing, better quality and more environmentally friendly

(1) Compared with the traditional drawing process, the phosphating and saponification treatment processes are reduced, and the product is more environmentally friendly.

(2) Special processing technology gives the product's internal and external quality a qualitative leap, and all parameters meet or exceed standards.

(3) Special thinning technology makes the product lighter and easier to carry.

KAIGEN seamless gas cylinders are more suitable for cylinder wall and internal environment treatment (ground, electrochemically polished, internally coated) than seamless gas cylinders of other brands. KAIGEN seamless gas cylinders are more suitable for ultra-high purity gases.

Please click on the hyperlink to view: What is special about KAIGEN and LEO's seamless steel gas cylinders?